Record Details

KINETIKA REAKSI PEMBENTUKAN TRIKALSIUM PHOSPHATE (Ca3(PO4)2) DARI KALSIUM KARBONAT BERBAHAN BAKU CANGKANG KUPANG PUTIH

Journal of Research and Technology

View Archive Info
 
 
Field Value
 
ISSN 2477-6165
2460-5972
 
Authentication Code dc
 
Title Statement KINETIKA REAKSI PEMBENTUKAN TRIKALSIUM PHOSPHATE (Ca3(PO4)2) DARI KALSIUM KARBONAT BERBAHAN BAKU CANGKANG KUPANG PUTIH
 
Added Entry - Uncontrolled Name Pujiastuti, Caecilia
Nofitasari, Luluk
Erfani, Rif’atul Firda
Universitas Pembangunan Nasional “Veteran” Jawa Timur
Universitas Pembangunan Nasional “Veteran” Jawa Timur
Universitas Pembangunan Nasional “Veteran” Jawa Timur
 
Summary, etc. The development of the health sector to search alternatife material bone’s repair is increasing. Bone is a natural composite containing 60% minerals, 30% matrix, and 10% water. The component of bone mineral is calcium phosphate. Tricalcium phosphate is the type of calcium phospate that used because it has chemical component’s as like bone’s component. In this study, white mussel shell was chosen as a source of calcium and H3PO4 as a solvent. The aim of this research was determining reaction kinetics of tricalcium phospate synthesis from white mussel shells. The research was started by dissolving 50 grams of white mussel shell in 1 L of H3PO4 3% at reaction time with variation 2, 4, 6, 8, 10 minutes and reaction temparature with variation 40, 50, 60, 70, 80oC and then filtered. The filtrate was analyzed for the content of phosphoric acid while the residue was calcined at 900oC for 5 hours to remove the water. The reaction rate increased with increasing time and temperature. The highest phosphate acid conversion was obtained at a temperature of 80 ° C, with a reaction time of 10 minutes is 90.92%. The controlling step that controlled tricalcium phosphate synthesis from white mussel shell followed pseudo first-order equation with the Arrhenius equation.The results of XRD analysis found that89%of Ca3(PO4)2was formed.
 
Publication, Distribution, Etc. 2477 - 6165
 
Electronic Location and Access application/pdf
https://journal.unusida.ac.id/index.php/jrt/article/view/149
 
Data Source Entry Journal of Research and Technology; Vol. 6 No. 1 (2020): JRT Volume 6 No 1 Jun 2020
 
Language Note eng
 
Terms Governing Use and Reproduction Note Copyright (c) 2020