ANALISIS KEKUATAN TARIK, KEKERASAN, DAN STRUKTUR MIKRO PADA PENGELASAN BAJA ST-60 BERDASARKAN VARIASI TEMPERATUR TEMPERING

G-Tech: Jurnal Teknologi Terapan

View Archive Info
 
 
Field Value
 
Title ANALISIS KEKUATAN TARIK, KEKERASAN, DAN STRUKTUR MIKRO PADA PENGELASAN BAJA ST-60 BERDASARKAN VARIASI TEMPERATUR TEMPERING
 
Creator Pradani, Yayi Febdia
Aziza, Yuliana
Rahmat, Muhammad Hudan
 
Description Tujuan penelitian ini untuk mengetahui adanya pengaruh variasi temperatur tempering pada temperatur 2500C, 3500C, dan 5000C dengan holding time 30 menit menggunakan pendinginan udara terhadap kekuatan tarik, kekerasan dan struktur mikro pada pengelasan baja St.60. Metode dalam penelitian ini menggunakan deskriptif kuantitatif. Sedangkan desain penelitiannya adalah penelitian eksperimental yang dilakukan di laboratorium. Objek penelitian ini adalah baja karbon menengah St.60 yang kemudian diberi perlakuan yakni pengelasan kemudian tempering dengan variasi temperatur.Hasil penelitian rata-rata kekuatan tarik tertinggi diperoleh pada temperatur tempering 5000C sebesar 680,495 MPa, pada temperatur 3500C sebesar 666,016 MPa, dan kekuatan tarik terendah diperoleh pada temperatur tempering 2500C sebesar 641,626 MPa. Sedangkan kekerasan tertinggi diperoleh pada temperatur tempering 5000C sebesar 284,87 Hv, pada temperatur 3500C sebesar 267,63 Hv, dan kekerasan terendah diperoleh pada temperatur tempering 2500C sebesar 259,111 Hv. Hal ini menunjukkan bahwa terdapat perbedaan nilai kekuatan tarik dan kekerasan pada baja St.60 antara sebelum dan setelah mengalami proses tempering dengan variasi temperatur sehingga dapat disimpulkan bahwa vaiasi temperatur tempering berpengaruh terhadap tingkat kekuatan tarik dan kekerasan pada pengelasan baja St.60. Tingkat kekuatan tarik dan kekerasan baja akan meningkat seiring bertambahnya temperature tempering pada pengelasan baja St.60.
This research use for to know how at temperatures of 2500C, 3500C, and 5000C with a holding time of 30 minutes using air against the strength of tensile, defense and microstructure in the welding of steel St. 60. This research method uses descriptive quantitative. While the research design is experimental research conducted in the laboratory. The object of this research is the medium carbon steel St. 60 which was then named as welding then tempering with temperature variations. The results of the highest average tensile strength were obtained at 5000C tempering temperature of 680,495 MPa, at 3500C at 666,016 MPa, and can be recovered at 2500C tempering temperature of 641,626 MPa. While the highest temperature was obtained at 5000C tempering temperature of 284.87 Hv, at a temperature of 3500C at 267.63 Hv, and the lowest hardness was obtained at 2500C tempering temperature of 259,111 Hv. 60 before and after the hardening process with temperature variations can be used to determine the temperature hardening to the level of tensile strength and defense in steel welding St.60. The level of tensile strength and protection of steel will increase as the tempering temperature increases in welding steel St.60.
 
Publisher Universitas Islam Raden Rahmat Malang
 
Date 2020-09-02
 
Type info:eu-repo/semantics/article
info:eu-repo/semantics/publishedVersion
Artikel Peer-review
 
Format application/pdf
 
Identifier https://ejournal.uniramalang.ac.id/index.php/g-tech/article/view/327
10.33379/gtech.v2i1.327
 
Source G-Tech: Jurnal Teknologi Terapan; Vol. 2 No. 1 (2018): G-Tech Oktober 2018; 98-105
G-Tech: Jurnal Teknologi Terapan; Vol 2 No 1 (2018): G-Tech Oktober 2018; 98-105
2623-064X
2580-8737
10.33379/gtech.v2i1
 
Language ind
 
Relation https://ejournal.uniramalang.ac.id/index.php/g-tech/article/view/327/360
 
Rights Hak Cipta (c) 2018 G-Tech : Jurnal Teknologi Terapan
https://creativecommons.org/licenses/by/4.0